Uso y caracterización de recubrimientos de TiO2 producidos por Depositación centrífuga (Spin Coater) como detector de contaminante

Abstract

In this work are sintetizoTiO2 by the Sol-Gel method to obtain coatings of one, two and three layers deposited by the technique of spinning (Spin coating) once obtained the coatings were dried at 90 °C, and subjected to heat treatments of 350, 450 and 550 °C for 1 hour. The coatings obtained were performed the following specifications: Ultraviolet Visible (UV-VIS), Interferometry, diffuse and specular reflectance. In addition to electrical tests on current against voltaje. Tests were carried out for heterogeneous photocatalysis to degrade methylene blue to a concentration of 20 ppm, to two different temperatures at 20 °C ambient temperature and 50 °C.

En este trabajo se sintetizoTiO2 por el método Sol-Gel para obtener recubrimientos de una, dos y tres capas depositados por la técnica de centrifugado (Spin Coating) una vez obtenidos los recubrimientos fueron secados a 90 °C, y sometidos a tratamientos térmicos de 350, 450 y 550 °C durante 1 hora. Los recubrimientos obtenidos se les realizaron las siguientes caracterizaciones: Ultravioleta Visible (UV-VIS),Interferómetria, Reflectancia Difusa y Especular. Además de hacerse pruebas eléctricas de corriente contra voltaje. Se realizaron pruebas de fotocatálisis heterogénea para degradar Azul de Metileno a una concentración de 20 ppm, a dos distintas temperaturas, a 20°C temperatura ambiente y a 50°C.