Procesamiento y caracterización de TiC empleando mecanosíntesis

Abstract

In this paper the synthesis of titanium carbide TiC is presented using the mechanical alloying (AM), from elemental titanium and graphite powders trade. The synthesis was performed at room temperature using a SPEX 8000 mill high energy. The powders were subjected to different milling times and under specific conditions, thus, finding the time in which the alloy is completely and with a minimum percentage of contamination. The evolution of the powders during processing and analysis structural alloy, was conducted through characterization techniques X-ray diffraction (XRD), scanning electron microscopy (SEM) and Transmission electron microscopy (TEM). The results obtained by TEM and XRD were processed using specialized software, Full prof- Suite, CRISP and Digital Micrograph.

En este trabajo se presenta la síntesis del carburo de titanio TiC empleando el aleado mecánico (AM), a partir de polvos elementales de titanio y grafito comerciales. Esta síntesis se realizó a temperatura ambiente y utilizando un molino SPEX 8000 de alta energía. Los polvos fueron sometidos a diferentes tiempos de molienda y bajo condiciones específicas, para así, encontrar el tiempo en el cual la aleación se forma completamente y con un porcentaje mínimo de contaminación. La evolución de los polvos durante el proceso, así como el análisis estructural de la aleación, se realizó a través de las técnicas de caracterización de difracción de rayos-X (DRX), microscopía electrónica de barrido (MEB) y microscopía electrónica de transmisión (TEM). Los resultados obtenidos por TEMy DRX se procesaron utilizando software especializado, Fullprof- Suite, CRISP y Digital Micrograph.