Mecanosíntesis de ceria dopada con tierras raras

Abstract

In recent years have sought new alternatives for energy production due to depletion of nonrenewable natural resources, some devices that have been found are fuel cells solid oxide (SOFC-solid oxide fuel cell) with electrolyte composite material ceramic. Among the acceptable materials having ionic conductivity is yttria stabilized zirconia (YSZ) (S / cm at 1000 ° C, 8YSZ, ZrO2-8 mol% Y 2 O 3), the disadvantage is its high operating temperature it significantly increasing the cost, this is a major cause to find alternative materials having ionic conductivity similar to yttria stabilized zirconia operating at lower temperatures.

En los últimos años se han buscado nuevas alternativas para la producción de energía debido al agotamiento de recursos naturales no renovables, algunos dispositivos que se han encontrado son las celdas de combustible de óxido sólido (SOFC-solid oxide fuel cell) con electrolito compuesto de material cerámico. Entre los materiales que presentan conductividad iónica aceptable se encuentra la zirconia estabilizada con itria (YSZ) o=0.17( S/cm a 1000°C, 8YSZ, ZrO2 -8 mol% Y 2 O 3 ), la desventaja es su elevada temperatura de operación lo que aumenta significativamente el costo, esta es una de las causas principales de buscar materiales alternativos que presenten conductividad iónica semejante a la zirconia estabilizada con itria que operen a temperaturas menores.