Producción y caracterización de uniones Al2O3/Ti empleando metalizados de Nb y Mo

Abstract

In this research study, he worked with the company Greatbatch Medical doctor bouquet in the interfacial study of metal / ceramic devices manufactured by the method of brazing (Brazing by an English translation). Devices have a special design consisting of a metallized ceramic part Al2O3 pure Nb or Mo, gold rings as filling material and a housing made from a Ti-grade 4 biocompatibility properties. Samples were attached to a temperature of 1090 ° C with residence times of 0, 2.5 and 5 minutes in a high vacuum oven. Furthermore, the thickness of metallic samples using unmetallized, 2 microns thick, to which was referenced as "standard metallic" and 4 microns as "metallic double" was varied.

En el presente estudio de investigación, se trabajó en conjunto con la empresa del ramo médico Greatbatch Medical en el estudio interfacial de dispositivos metal/cerámico fabricados por la empresa por el método de soldadura fuerte (Brazing por su traducción al inglés). Los dispositivos tienen un diseño especial que consta de una pieza cerámica de Al2O3 pura metalizada con Nb o Mo, anillos de oro como material de aporte y una carcasa hecha a base de una aleación de Ti grado 4 con propiedades de biocompatibilidad. Las muestras fueron unidas a una temperatura de 1090°C con tiempos de permanencia de 0, 2.5 y 5 minutos en un horno de alto vacío. Por otro lado, se varió el espesor del metalizado empleando muestras sin metalizar, con 2 μm de espesor, a las que se referenció como “metalizado estándar” y de 4 μm como “doble metalizado”.