Evaluación de la reacción de fragilización ambiental por hidrógeno en intermetálicos Al-Ni inducida por molienda mecánica en húmedo

Abstract

The present research is related to the mechanical milling process (MM) of the intermetallic Al3Ni high energy at different times. This process is characterized by non-equilibrium processing, which consists in supplying energy to a material in a dynamic external comminution process, resulting in a "boost" to a metastable state. These conditions favor the sintering process nonequilibrium phases such as solid solutions, quasicrystalline phases and crystalline phases, phase transformations, amorphous alloys and nanostructures. Furthermore, the mechanical milling process improves the physical, chemical and mechanical properties of materials, providing better applications.

La presente investigación está relacionada con el proceso de molienda mecánica (MM) de alta energía del intermetálico Al3Ni a diferentes tiempos. Este proceso se caracteriza por ser un procesamiento fuera de equilibrio, que consiste en el suministro de energía a un material en un proceso dinámico de conminución externo, lo que resulta en un "impulso" hacia un estado metaestable. Estas condiciones favorecen el proceso de sinterización de fases fuera del equilibrio tales como soluciones sólidas, fases cristalinas y fases cuasicristalinas, transformaciones de fase, aleaciones amorfas y nanoestructuras. Por otro lado, el proceso de molienda mecánica mejora las propiedades físicas, químicas y mecánicas de los materiales, proporcionando mejores aplicaciones.