Síntesis y caracterización de nanomateriales de CsPbCl₃ y Cs4PbCl6

Abstract

The present thesis work is presented the synthesis and characterization of 2D nanosheets shaped nanomaterials of CsPbCl3 and Cs4PbCl6 with perovskite structure. They were synthesized by the hot injection method with variations in temperature and reaction times. In addition, TOP was added to the method, which considerably helped the dissolution time of the PbCl3 precursor. Nanosheets were obtained with dimensions between 100 nm to 1.2 μm in length and width, with thicknesses between 10 nm to 50 nm. It was found that the variation of nanosheet sizes was due to the amount of ligands (OA) and the thickness of nanosheets is associated with the change of reaction temperature from 150, 170, 200 °C. In addition, the nanosheets that were synthesized at the lowest temperature are the ones that had the best absorbance and photoluminescence.

En este trabajo de tesis se presenta la síntesis y caracterización de nanomateriales 2D con forma de nanohojas de CsPbCl3 y Cs4PbCl6 con estructura perovskita. Se sintetizaron por el método de inyección en caliente haciendo variaciones de temperatura y tiempos de reacción. Adicional al método se le agregó TOP que ayudó considerablemente el tiempo de disolución del precursor PbCl3. Se logró obtener las nanohojas con dimensiones de entre 100 nm a 1.2 μm de largo y ancho, con grosores entre 10 nm a 50 nm. Se encontró que la variación de los tamaños de la nanohoja se debió a la cantidad de ligandos (OA) y el espesor de las nanohojas se asocia al cambio de la temperatura de reacción de 150, 170, 200 °C. Además, las nanohojas que se sintetizaron a la temperatura más baja son las que tuvieron una mejor absorbancia y fotoluminiscencia.