In this research the effect of additions of boron (less than 195 ppm) in a high chromium white iron (17% Cr-2.5% C) directionally solidified analyzed. Due to the high level of segregation during solidification having a constitutional boron overcooling in austenite amending the solidification rate of the leading sub-phase (austenite) is generated, so that a change occurs solidification mechanism accompanied by a refinement of the microstructure of the iron. Microanalysis composition were performed using a scanning electron microscope, determining the chemical distribution within the phases forming the microstructure, where it was observed that the boron segregates to the austenite / carbide interface and this is mainly dissolved in the eutectic carbide, some sometimes forming a boron compound.
En esta investigación se analiza el efecto de adiciones de boro (menores a 195 ppm) en un hierro blanco alto cromo (17% Cr-2.5% C) solidificado direccionalmente. Debido al alto nivel de segregación durante la solidificación que presenta el boro se genera un sobre-enfriamiento constitucional en la austenita que modifica la velocidad de solidificación de la fase sub-líder (austenita), por lo que se presenta un cambio el mecanismo de solidificación, acompañado de un refinamiento de la microestructura del hierro. Se realizaron microanálisis de composición usando un microscopio electrónico de barrido, determinando la distribución química dentro de las fases que forman la microestructura, donde se observó que el boro segrega hacia la interfase austenita/carburo y este se encuentra principalmente disuelto en el carburo eutéctico, algunas veces formando un compuesto de boro.