Plates (6.35 mm thick) of 2205 duplex stainless steel (DSS) with a single V groove preparation were gas metal arc welded in a single pass using an ER-2209 filler wire. Welding parameters were adjusted to input 1.4 kJ/mm using two gas mixtures; 98 % Ar + 2 % O2 (M1) y 97 % Ar + 3 % N2 (M2). With mixture M1 welds were made with electromagnetic interaction of low intensity (EMILI) applying external electromagnetic fields (EEMF) of 0, 3, 6, 9, 12 and 15 mT. The welds were subjected to macro and microstructural characterization as well as mechanical and electrochemical evaluation. It was found that EMILI reduces the size of the high temperature heat affected zone (HTHAZ) and increases the ratio of molten base metal (BM) due to the electromagnetic stirring (EMS) of the weld pool.
Se soldaron en una pasada placas (6.35 mm) con preparación en simple V de la aleación de acero inoxidable dúplex 2205 (AID), usando el electrodo ER-2209 con el proceso de soldadura por fusión con arco metálico y protección gaseosa (GMAW). Las variables operativas de soldadura se ajustaron para aportar 1.4 kJ/mm utilizando dos mezclas de gases; 98% Ar + 2% O2 (M1) y 97% Ar + 3% N2 (M2). Con la mezcla M1 se realizaron las soldaduras con interacción electromagnética de baja intensidad (IEMBI) aplicando campos electromagnéticos externos (CEME) de0, 3, 6, 9, 12 y 15 mT. A las soldaduras se les realizó la caracterización macro y microestructural, mecánica y electroquímica. Se encontró que la IEMBI disminuye la zona afectada térmicamente de alta temperatura (ZATAT) e incrementa la relación de metal base (MB) fundido por efecto de la agitación electromagnética (AEM) del metal de soldadura (MS).