Precipitación de la fase sigma bajo la aplicación de ciclos térmicos en un acero inoxidable superdúplex SAF 2507

Abstract

Superduplex Stainless steel is used mainly in industry chemical, petrochemical and oil and consisting of approximately 50% 50% ferrite and austenite, which enables a combination of excellent mechanical properties and high corrosion resistance. The characteristics and properties offered by superduplex stainless steels, are due to the contents of Cr, Mo, Ni and N, which also promote sigma phase formation. This phase is significantly harmful, and therefore, its presence in superduplex stainless steel is undesirable because is comprised mainly of Cr and Mo, which causes a decrease in corrosion resistance and mechanical properties. Sigma phase shape function of time and temperature, so the stainless steel superduplex is highly susceptible to the precipitation of this phase in the range of approximately 600-950 ° C.

El acero inoxidable superdúplex es utilizado principalmente en la industria química, petroquímica y del petróleo ya que consiste aproximadamente de 50% ferrita y 50% austenita, lo que permite una combinación de excelentes propiedades mecánicas y una elevada resistencia a la corrosión. Las características y propiedades que ofrecen los aceros inoxidables superdúplex, se deben a los contenidos de Cr, Mo, Ni y N, los cuales también promueven la formación de fase sigma. Esta fase, es significativamente dañina, y por lo tanto, su presencia en los aceros inoxidables superdúplex es indeseable debido a que se forma principalmente por Cr y Mo, lo que provoca una disminución de su resistencia a la corrosión y de sus propiedades mecánicas. La fase sigma se forma en función del tiempo y la temperatura, por lo que el acero inoxidable superdúplex es altamente susceptible a la precipitación de esta fase en el rango de 600 a 950°C aproximadamente.