By the sol-gel route, the route using acetic acid, PZT powders were obtained in the compositions: 57/43, 53/47, 50/50, 45/55, 40/60. These were characterized by XRD, scanning electron microscopy and Differential Scanning Calorimetry obtaining a crystalline phase with small traces of pyrochlore, they disappear with treatment at 700 C for 4 hrs. We obtained a particle size of 8.5 nm to 9.2 tetragonal and rhombohedral compositions for compositions. And a Curie temperature of 320 ° C. From these several pills which were sintered at 900, 1000 and 1100 ° C obtaining a pyroelectric of different pills against a polarization curve, obtaining a voltage of 290 mV CD with an electric field of 3 kV / mm type units they were developed, as expected, the best responses were near the morphotropic line (53/47), the higher the field and based on perfectly crystallized powders.
Por medio de la vía sol-gel, usando la ruta del ácido acético, se obtuvieron polvos de PZT en las composiciones: 57/43, 53/47, 50/50, 45/55, 40/60. Estos fueron caracterizados por Difracción de rayos X, Microscopía electrónica de barrido y Calorimetría diferencial de barrido obteniéndose una fase cristalina con pequeñas trazas de pirocloro, las mismas desaparecen con un tratamiento a 700º C por 4 hrs. Obtuvimos un tamaño de partícula de 8.5 nm para las composiciones tetragonales y 9.2 para las composiciones romboédricas. Y una temperatura de Curie de 320 ºC. A partir de ellos se elaboraron varias unidades tipo pastillas las cuales se sinterizaron a 900, 1000 y 1100º C obteniéndose una piroeléctrica de las diferentes pastillas contra una curva de polarización, obteniéndose un voltaje de 290 mV CD con un campo eléctrico de 3kV/mm, tal como se esperaba, las mejores respuestas se dieron cerca de la línea morfotrópica (53/47), a mayor campo y partiendo de polvos perfectamente cristalizados.