This research was focused on the examination of mini implants made of titanium alloy Ti-6Al-4V used for orthodontics applications. The mini implants were anchored on three patients during four months. After being removed, mini implants were analyzed by means of optical microscopy as well as scanning electron microscopy in order to determine surface changes, microstructural changes and some differences on chemical composition on every mini implant. Results showed that mini implants experienced wear on the thread promoting a hardness increment in that area. However, there is no significant difference in the chemical composition on the different areas of every mini implants analyzed.
La presente investigación fue enfocada a examinar mini implantes fabricados de Ti-6Al-4V para uso ortodóncico, los cuales fueron empleados en pacientes por un periodo de 4 meses. Después de haber sido retirados, los mini implantes fueron analizados mediante microscopía óptica y microscopía electrónica de barrido para determinar cambios superficiales, microestructrales y diferencias en la composición química. Los resultados muestran que los mini implantes presentan desgaste en la sección de la rosca, lo cual promueve un incremento de dureza en la superficie de esta sección, sin embargo, no existe una diferencia significativa en la composición química en las diferentes secciones de cada uno de los mini implantes.