Water contamination is a problem that affects all ecosystems and directly to human beings, the reserves for our consumption are increasingly scarce and disinfection methods are expensive and ineffective. In this work, a TiO2-based material was synthesized by the sol-gel method, which was doped with Ce, and Ag was added by the incipient humidity method, with the purpose of giving it a bactericidal effect against Staphylococcus aureus, Escherichia coli, Shigella sonnei, Salmonella typhimurium bacteria strains and a consortium of these to simulate a more real environment. It was characterized by XRD techniques to observe the phases of the material, as well as the crystal size, SEM to observe the morphology of the material and its surface, BET, to obtain the surface area, pore size and volume and finally by IR spectroscopy, to observe the bonds presented by the material.
La contaminación del agua es un problema que afecta a todos los ecosistemas y directamente a los seres humanos, las reservas para nuestro consumo son cada vez más escasas y los métodos de desinfección son costosos y poco efectivos. En este trabajo se sintetizó mediante el método de sol-gel un material a base de TiO2, que fue dopado con Ce, y mediante el método de humedad incipiente se le agregó Ag, cuya finalidad es darle un efecto bactericida contra las cepas de bacterias Staphylococcus aureus, Escherichia coli, Shigella sonnei, Salmonella typhimurium y un consorcio de estas para simular un ambiente más real. Se caracterizó mediante las técnicas, DRX para observar las fases del material, así como el tamaño de cristal, SEM para observar la morfología del material y su superficie, BET, para obtener el área superficial, tamaño y volumen de poro y por ultimo por espectroscopia IR, para observar los enlaces que