In the present research project, a printed support with 3D technology was made with polylactic acid as printing material. The enrichment and stabilization of anaerobic sludge from an Upflow Anaerobic Reactor (UASB) was carried out, feeding it with pig manure, performing a physicochemical monitoring with parameters such as pH, alkalinity, ? ratio, volatile fatty acids, afther the anaerobic sludge was stabilized, the 3D structures were inoculated under pretreatment conditions with nopal mucilage. By weight difference, the formation of a biofilm on the 3D printed material was corroborated. The best results were obtained by submerging the structure in nopal mucilage for 24 hours, and weekly feeding the anaerobic inoculum with pig manure. It was determined that the development of a biofilm is proportional to the roughness presented on the growth surface.
En el presente proyecto de investigación se realizó un soporte impreso con tecnología 3D con ácido poliláctico como material de impresión. Se realizó el enriquecimiento y estabilización de lodo anaerobio proveniente de un Reactor Anaerobio de Flujo Ascendente (RAFA) alimentándolo con estiércol de cerdo, realizando un seguimiento fisicoquímico con parámetros como pH, alcalinidad, relación α, ácidos grasos volátiles (AGV´S), una vez estabilizado el lodo anaerobio se realizó la inoculación de las estructuras 3D bajo condiciones de pretratamiento con mucílago de nopal. Mediante diferencia de peso se corroboró la formación de una biopelícula sobre el material impreso en 3D. Los mejores resultados se obtuvieron al sumergir durante 24 horas la estructura en mucílago de nopal, y alimentando semanalmente el inoculo anaerobio con estiércol de cerdo. Se determinó que el desarrollo de una biopelícula es proporcional a la rugosidad presentada en la superficie de crecimiento.