The synthesis of alternative materials and novel magnesium-based high-AlN for applications in electronic packaging and thermal control is the main objective of the present work. Composites were produced by a technique of capillary infiltration liquid magnesium AlN porous preform under a controlled argon at a temperature of 900 °C atmosphere; preforms were previously compacted and uniaxially cold-sintered in nitrogen in order to provide strength for better handling and avoid fracture during the infiltration stage. The aluminum nitride content in the composites was ~60% volume; materials were designed with high ceramic content in order to obtain a low coefficient of thermal expansion and high thermal conductivity characteristics indispensable proposed applications for these materials.
La síntesis de materiales alternativos y novedosos base magnesio con alto contenido de AlN para aplicaciones en el empaquetamiento electrónico y el control térmico es el principal objetivo del presente trabajo. Se fabricaron compósitos mediante una técnica de infiltración capilar de magnesio líquido en preformados porosos de AlN bajo una atmósfera controlada de argón a una temperatura de 900 °C; previamente las preformas fueron compactadas uniaxialmente en frío y presinterizadas en nitrógeno con la finalidad de proveer resistencia para una mejor manejabilidad y evitar su fractura durante la etapa de infiltración. El nitruro de aluminio contenido en los compósitos fue de ?60% volumen; los materiales fueron diseñados con alto contenido cerámico con la finalidad de obtener un bajo coeficiente de expansión térmico y una alta conductividad térmica, características indispensables en las aplicaciones propuestas para estos materiales.