In this investigation fine silver oxide powders were used and Molybdenum, which were mechanically ground to distribute homogeneously both phases further reduce their particle size. These mixtures were used to study the kinetics of reduction, with hydrogen and associated control mechanisms in the formation of silver-molybdenum alloys. A thermogravimetric balance was used to follow the progress of the reduction with respect to time. First is to studies conducted reduction kinetics for Ag 2 O and MoO 3 in ranges temperature of 348-398 K and 893-953 K, respectively. As range temperature reduction of Ag 2 O and MoO 3 is very broad; kinetics Mixdowns with molar ratios of 1: 1, 1: 2, 1: 4, study Non-isothermal manner using a heating rate of 11 K / min., and hydrogen as the reducing gas.
En esta investigación se utilizaron polvos finos de óxidos de plata y molibdeno, Los cuales fueron molidos Mecánicamente Para distribuir homogéneamente ambos fases, además, de reducir su tamaño de partícula. Estas mezclas fueron utilizadas para estudiar la cinética de reducción, con hidrogeno, así como los mecanismos de control asociados en la formación de aleaciones plata-molibdeno. Se utilizó una balanza termogravimetrica seguir el progreso de la reducción con respecto al tiempo. Para Primeramente se realizaron estudios de cinética de reducción para el Ag2O y MoO3 en rangos de temperatura de 348 a 398 K y de 893 a 953 K, respectivamente. Como el rango de temperatura de reducción de Ag2O y MoO3 es muy amplio; la cinética de reducción de mezclas con relaciones molares de: 1:1, 1:2, 1:4, se estudió de manera no isotérmica utilizando una rampa de calentamiento de 11 K/min., e hidrogeno como gas de reductor.