During the last three decades the CaO content in concrete Traditional refractory castable was up 20%. This generated large disadvantages to reduce the refractory properties of materials industry due to its high content of CaO, in addition to the produce requiring much water resulting in low density and high porosity. Subsequently emerged developing specific low and ultra-low cement involves replacing the contents of CaO oxides silicon, aluminum, titanium or chromium to improve the quality of concrete pourable including flow properties. This paper makes a study on the problems associated with the replacement of calcium aluminate cement colloidal silica in the refractory castable concrete by various granulometries components and formulations according to the equation Furnas for optimal packing of particles up samples.
Durante las últimas tres décadas el contenido de CaO en los concretos refractarios colables tradicionales era hasta de 20%. Esto generó grandes desventajas al disminuir las propiedades en la refractariedad de los materiales industriales debido a su alto contenido de CaO, además de que al producirlos requerían de mucho agua dando como resultado baja densidad y alta porosidad. Posteriormente surgió el desarrollo de los concretos de bajo y ultrabajo cemento que consiste en reemplazar el contenido de CaO por óxidos de silicio, aluminio, titanio o cromo que mejoran la calidad de los concretos colables incluyendo las propiedades de fluidez. Este trabajo hace un estudio sobre la problemática asociada a la sustitución del cemento cálcico aluminoso por silica coloidal en los concretos refractarios colables mediante diferentes formulaciones de componentes y granulometrías de acuerdo a la ecuación de Furnas para obtener un empaquetamiento óptimo de las partículas que componen las muestras.