This paper presents a detailed study of the synthesis and processing of a series of mixed oxides of zirconia-alumina system (ZrO 2 -Al 2 O 3) for possible implementation as catalysts and catalyst supports. The ceramic powders containing 0, 10, 25, 50 to 100 weight% alumina were prepared by sol-gel precursors based on inorganic and using polystyrene beads (EP) with diameters of 685 and 1520 nm templates agents, which were synthesized by the polymerization process emulsion. Porous structures for the various compositions were obtained by two different synthetic routes, both based on colloidal processing of ceramic gels templates assisted. The physicochemical characterization of the synthesized materials was conducted by the techniques of X-ray Diffraction (XRD), gas adsorption (S BET), Infrared Spectroscopy (FT-IR), electron microscopy (SEM), thermal analysis (DSC) and measurements Zeta potential.
El presente trabajo muestra un estudio detallado acerca de la síntesis y procesamiento de una serie de óxidos mixtos del sistema zirconia-alúmina (ZrO 2 -Al 2 O 3 ) para su posible aplicación como catalizadores y soportes catalíticos. Los polvos cerámicos con contenidos de 0, 10, 25, 50 y 100 % peso de alúmina fueron preparados por la técnica sol-gel partiendo de precursores inorgánicos y utilizando esferas de poliestireno (EP) con diámetros de 685 y 1520 nm como agentes templantes, las cuales fueron sintetizadas por el proceso de polimerización por emulsión. Las estructuras porosas para las diferentes composiciones, fueron obtenidas por dos diferentes rutas de síntesis, ambas basadas en el procesamiento coloidal de los geles cerámicos asistido por templantes. La caracterización fisicoquímica de los materiales sintetizados se llevó a cabo por las técnicas de Difracción de rayos-X (DRX), Adsorción de gases (S BET ), Espectroscopia de Infrarrojo (FT-IR), Microscopía electrónica de Barrido (MEB), Análisis Térmico (DSC) y mediciones de Potencial Zeta.