In the present study, a series of magnetic hexaferrites oxides were synthesized from Bario pure BaFe12O19 and replaced [Ba(CoxTix) Fe12-2xO19], with values 0 ≤ x ≤ 0.6. the ceramic powders were synthesized by the coprecipitation method starting from using inorganic precursors and a surfactant, followed by processing with microwave irradiation times 0, 2, 4 and 6 minutes. The effect of the route of synthesis and the incorporation of Ti and Co captions in the structural parameters, microstructural and magnetic properties of the hexaferrites were studied. The characterization of the samples was carried out by thermal analysis techniques (DTA-TGA), X-ray Diffraction (XRD), scanning electron microscopy (SEM) and measurement of magnetic properties was conducted using a sample magnetometer Vibrant (MMV).
En el presente estudio, se sintetizaron una serie de óxidos magnéticos de Hexaferritas de Bario puras BaFe12O19 y sustituidas [Ba(CoxTix )Fe12-2xO19], con valores 0 ≤ x ≤ 0.6 . Los polvos cerámicos fueron sintetizados por el método de coprecipitación partiendo de precursores inorgánicos y utilizando un agente surfactante, seguido de su procesamiento por microondas con tiempos de irradiación de 0, 2, 4 y 6 minutos. El efecto de la ruta de síntesis y de la incorporación de los cationes Ti y Co en los parámetros estructurales, microestructurales y propiedades magnéticas de las hexaferritas fueron estudiados. La caracterización de las muestras se llevó a cabo por las técnicas de Análisis Térmico (ATD-ATG), Difracción de Rayos-X (DRX), Microscopía Electrónica de Barrido (MEB) y la medición de propiedades magnéticas se realizó mediante un Magnetómetro de Muestra Vibrante (MMV).