Determinación de la cinética de corrosión en los aceros inoxidables sensibilizados AISI 316 y 430 inducidos por bacterias termófilas sulfato reductoras a 70 °C

Abstract

To isolate the bacteria that was induced corrosion on steel AISI 316 and 430, a sample of water vapor condensates Unit was taken Geotermoeléctrico Tejamaniles the field of Azufres, Michoacán. This shows was inoculated in various culture media at 70 ° C, and selecting the middle of proper growth. Later a colony of bacteria was isolated sulfate reducing. AISI 316 steel specimens and 430 1 cm 2 were cut and one sensitized of them at 650 ° C and 950 ° C. After being roughened and degreased, is they contacted the sulfate-reducing bacteria. By measuring pH, determining the concentration of acid hydrogen, performing electrochemical polarization tests and analysis surface, the said microorganisms induced corrosivity was determined and evaluated the effect of awareness in each of the steels.

Para aislar la bacteria con la que se indujo la corrosión en los aceros AISI 316 y 430, se tomó una muestra de agua de los condensados de vapor de la Unidad Tejamaniles del campo geotermoeléctrico de los Azufres, Michoacán. Esta muestra fue inoculada en diversos medios de cultivo a 70°C, y seleccionar el medio de crecimiento adecuado. Posteriormente se aisló una colonia de bacterias sulfato reductoras. Se cortaron probetas de acero AISI 316 y 430 de 1 cm 2 y se sensibilizaron una parte de ellas a 650°C y a 950°C. Después de ser desbastadas y desengrasadas, se pusieron en contacto con la bacteria sulfato reductora. Mediante la medición de pH, la determinación de la concentración del ácido sulfhídrico, la realización de pruebas electroquímicas de polarización y el análisis de superficie, se determinó la corrosividad inducida por dichos microorganismos y se evaluó el efecto de la sensibilización en cada uno de los aceros.