Abstract

The precipitation hardening 17-4 PH steel has been widely used, because it has a balanced combination of good mechanical properties and corrosion resistance. The working temperature of this steel is below 390 C. There is great concern in the industry since after prolonged exposure to this temperature, exhibit degradation of their properties caused by aging. NDT offer versatility for application in the characterization of materials and components, without producing any harmful effect on these and can be applied in service or quality control. In order that the components made from this material still in operation it is necessary that the degree of impairment, which may be by the thermoelectric potential is evaluated nondestructively.

El acero endurecible por precipitación 17-4 PH ha sido usado ampliamente, debido a que presenta una combinación balanceada de propiedades mecánicas y una buena resistencia a la corrosión. La temperatura de trabajo de este acero está por debajo de los 390 ̊C. Existe una gran preocupación en la industria ya que después de una exposición prolongada a esta temperatura, presentan degradación de sus propiedades, causada por envejecimiento. Los ensayos no destructivos ofrecen gran versatilidad, para su aplicación en la caracterización de materiales y componentes, sin producir algún efecto nocivo sobre estos y se pueden aplicar en condiciones de servicio o como control de calidad. Con el objeto de que los componentes fabricados con este material sigan en funcionamiento es necesario que se evalúe en forma no destructiva el grado de deterioro, la cual puede ser mediante el potencial Termoeléctrico.