In this paper the effect of self-elimination of cracks was studied by high temperature oxidation of compounds of Al2O3Ni particles reinforced. Compounds Ni/Al2O3 were prepared by the method of mixing powders aqueous solution α-Al2O3 with Ni(NO3)2 • 6H2O as a precursor of 5% vol. Ni, dried at 300°C, reduced in an atmosphere of Ar + 1% H2 at 600°C /12 h and consolidated using PECS (press electric current sintering) at 1400°C/5 minutes until reaching 98% of the theoretical density of the final compound. Surface cracks were induced by using a Vickers indenter. The pre-cracked samples were cured in air at temperatures between 1000 and 1300°C for residence times of 1 to 48 h. The experimental results showed that the crack suppression effect depends on both time and temperature.
En el presente trabajo se estudió el efecto de auto‐eliminación de grietas por oxidación a alta temperatura de compuestos de Al2O3 reforzados con partículas de Ni. Los compuestos Ni/Al2O3 fueron preparados por el método de solución acuosa mezclando polvos de α‐Al2O3 con Ni(NO3)2 •6H2O como precursor del 5% en vol. de Ni, secados a 300°C, reducidos en una atmósfera de Ar+1%H 2 a 600°C/12 h y consolidados usando PECS (pulse electric current sintering) a 1400°C/5 minutos alcanzando hasta el 98% de la densidad teórica del compuesto final. Las grietas superficiales fueron inducidas mediante el uso de un indentador vickers. Las muestras pre‐agrietadas fueron sanadas en aire a temperaturas entre 1000 y 1300°C por tiempos de permanencia de 1 a 48 h. Los resultados experimentales mostraron que el efecto de eliminación de grietas depende tanto del tiempo como de la temperatura.