In this research the effect of corrosion by sulfate-reducing bacteria (SRB) thermophilic 60 0 C induced studied in the base material (MB) and heat affected zone (HAZ) of API X-70 steel used in pipelines of oil industry. To isolate the crude oil BSR bacteriological medium "Postgate" was used. The experimental results allowed to characterize BSR colonies and incubated at 60 0 C. The colonies and bacteria were observed after the third day of incubation. MB samples and ZAT 1cm 2 were embedded in epoxy resin were prepared. The surface of the samples was gradually devastated using SiC abrasive paper of N0 400-1200 and then were exposed to a bacteriological medium periods; 5, 10, 20, 32 and 64 days. The electrochemical tests were employed; open circuit potential (GWP), polarization curves (CP) and electrochemical noise (RE).
En esta investigación se estudió el efecto de la corrosión inducida por Bacterias Sulfato Reductoras (BSR) termófilas de 60 0 C, en el material base (MB) y zona afectada térmicamente (ZAT), del acero API X-70 utilizado en oleoductos de la industria petrolera. Para aislar las BSR del petróleo crudo se utilizó el medio bacteriológico "Postgate". Los resultados experimentales permitieron caracterizar las colonias y las BSR incubadas a 60 0 C. Las colonias y bacterias, fueron observadas a partir del tercer día de incubación. Se prepararon muestras del MB y ZAT de 1cm 2 que fueron embutidas en resina epóxica. La superficie de las muestras se desbastó gradualmente utilizando papel abrasivo de CSi de N 0 400 hasta 1200 y posteriormente fueron expuestas a un medio bacteriológico a periodos de; 5, 10, 20, 32 y 64 días. Los ensayos electroquímicos empleados fueron; potenciales de circuito abierto (PCA), curvas de polarización (CP) y ruido electroquímico (RE).