In this research the effect of corrosion Sulfate Reducing Bacteria study (BSR) thermophilic to 60oC induced in the metal base (MB) and the welded joint (US) of API X-60 steel. Sulfate-reducing bacteria were isolated in the solid medium Postgate with the technique of striated, and were reseeded to get the same morphology. The average Postgate was selected among other culture media for optimal growth that present the BSR. MICROBIOLOGIC metal samples for testing and electrochemical base metal and the weld of the steel X-60 were prepared. The metal samples for microbiological testing were immersed in the culture medium Postgate with incubation periods of 5, 15 and 30 days at 60oC. Electrochemical tests were: curves potentiodynamic and electrochemical noise.
En esta investigación se estudió el efecto de la corrosión inducida por Bacterias Sulfato Reductoras (BSR) termófilas a 60oC en el metal base (MB) y la unión soldada (US) del acero API X-60. Las bacterias sulfato reductoras fueron aisladas en el medio sólido postgate con la técnica de estriado, y fueron resembradas hasta obtener la misma morfología. El medio postgate fue seleccionado entre otros medios de cultivo, por el óptimo crecimiento que presento la BSR. Se prepararon muestras metálicas para pruebas microbiologías y electroquímicas de metal base y de la unión soldada del acero X-60. Las muestras metálicas para las pruebas microbiológicas fueron inmersas en el medio de cultivo postgate con periodos de incubación de 5, 15 y 30 días a 60oC. Las pruebas electroquímicas fueron: curvas potenciodinámicas y ruido electroquímico.