In this thesis, the effect of electromagnetic stirring produced by an external magnetic field due to the application of a coil of copper wire 35.56 cm in diameter, during welding of API 5LX60 welded steel described submerged arc. This agitation, involves the refinement of columnar grain microstructure of the weld seam, which is produced by the same high heat input process. During experimentation, process monitoring sensors was performed using high Hall effect precision with which direct and indirect evidence that we determined the influence of the magnetic field on the refinement of columnar grain microstructure was obtained.
En el presente trabajo de tesis, se describe el efecto que tiene la agitación electromagnética producida por un campo magnético externo, debido a la aplicación de una bobina de alambre de cobre de 35.56 cm de diámetro, durante la soldadura de un acero API 5LX60 soldado por arco sumergido. Esta agitación, conlleva al refinamiento de grano de la microestructura columnar del cordón de soldadura, la cual es producida por el alto aporte térmico del mismo Proceso. Durante la experimentación, se realizó un monitoreo del proceso mediante sensores de alta precisión de efecto Hall, con los cuales se obtuvo información directa e indirecta que nos determinan la influencia del campo magnético sobre el refinamiento de la microestructura de grano columnar.