This paper studies the effect of small additions of a mixture of elements such as titanium, bismuth and rare earths, in the process of solidification of a eutectic low-chromium white iron commercially known as Ni-Hard Class I Type B according to ASTM standard A532. Ferrotitanium additions of rare-earths-Bismuth mixture (Fe-Ti-RE-Bi) in a low chromium white iron systematically to 2% were performed. Through these additions was achieved modifying the eutectic structure and the carbide phase change to a highly interconnected structure blocks smaller carbides and less ledeburítica interconnected structure. This microstructural change also caused changes in the mechanical behavior of the alloy.
El presente trabajo estudia el efecto de pequeñas adiciones de una mezcla de elementos como titanio, tierras raras y bismuto, en el proceso de solidificación eutéctica de un hierro blanco bajo-cromo conocido comercialmente como Ni-Hard Clase I Tipo B de acuerdo a la norma ASTM A532. Se realizaron adiciones de la mezcla Ferrotitanio-Tierras raras-Bismuto (Fe-Ti-RE-Bi) en un hierro blanco bajo cromo de manera sistemática hasta 2%. Por medio de estas adiciones se logró modificar la estructura eutéctica de la fase carburo y cambiarla de una estructura ledeburítica altamente interconectada a una estructura de bloques de carburos de menor tamaño y menos interconectados. Este cambio microestructural ocasionó también variaciones en el comportamiento mecánico de la aleación.