Influencia de la orientación del flujo magnético durante la soldadura del acero inoxidable 304, para mejorar las propiedades mecánicas en la zona afectada térmicamente (ZAT), mediante el proceso de soldadura MIG

Abstract

Welding of austenitic stainless steel with low intensity electromagnetic interaction is a recent welding method, which has resulted in the increased resistance to intergranular and pitting corrosion in the heat affected zone. Welding was performed in 6-mm thick with a single pass through GMAG process, with a shielding gas 98% Ar and 2% O2. This project austenitic 304 stainless steel with the same welding process was used, but for a thickness of 12.5 mm abutment with double V depositing two weld seams and single V depositing four cords, welding in the traditional way, with applying low intensity electromagnetic interaction and varying the direction of magnetic flux lines.

La soldadura del acero inoxidable austenítico con interacción electromagnética de baja intensidad es un método de soldadura reciente, el cual ha dado por resultado el incremento en la resistencia a la corrosión intergranular y por picado en la zona afectada térmicamente. La soldadura se ha realizado en placas de 6 mm de espesor con una sola pasada mediante el proceso GMAG, con un gas de protección 98% Ar y 2% de O2. El presente proyecto se utilizó el acero inoxidable austeníticos 304 con el mismo proceso de soldadura, pero para un espesor de 12.5 mm con unión a tope en doble V depositando dos cordones de soldadura y simple V depositando 4 cordones, soldando en forma tradicional, con la aplicando la interacción electromagnética de baja intensidad y variando el sentido de la líneas de flujo magnético.