In this work it was possible to manufacture the metal matrix composite AZ91E / TiC, using the technique of spontaneous infiltration 950⁰C for 24 minutes, starting from preformed porous sintered TiC previously, obtaining a 62% volume of TiC. Subsequently, the composite was subjected to a T6 heat treatment, by two stages under the following conditions: 1).- solubilization: 413⁰C for 24 h and 16 h, 2) .- artificially aged to: 216⁰C and 168⁰C for 1, 6, 12, 16 h at both temperatures. A thermodynamic analysis for AZ91E / TiC system, in order to predict the likely phases to form as the Gibbs free energy was performed.
En el presente trabajo se logró fabricar el material compuesto de matriz metálica AZ91E/TiC, mediante la técnica de infiltración espontánea a 950⁰C durante 24 minutos, partiendo de preformados porosos de TiC previamente sinterizados, obteniendo un 62% volumen de TiC. Posteriormente, el compósito fue sometido a un tratamiento térmico T6, mediante dos etapas con las siguientes condiciones: 1).- solubilización a: 413⁰C durante 24 h y 16 h, 2).- envejecido artificial a: 216⁰C y 168⁰C durante 1, 6, 12, 16 h en ambas temperaturas. Se realizó un análisis termodinámico para el sistema AZ91E/TiC, con el fin de predecir las fases probables a formarse según la energía libre de Gibbs.