Propiedades eléctricas y magnéticas de compósitos de matriz polimérica [Fe – Polímero]

Abstract

Induction heating has been a widely used method in heat treatments due to the reduction in heat, but a major drawback is the efficiency (about 70%). As a result concentrators have been developed magnetic energy, which is the study of this project. Magnetic energy concentrators must possess high initial magnetic permeability, low coercivity, high magnetic saturation and high electrical resistivity; to improve efficiency and resulting savings in electricity consumption. In this study polymer matrix composites obtained by uniaxial compaction six compaction pressures ranging from 1.5 kPa to 9.5 kPa, using Fe powders with particle size of ~ ~ 7μm and 109μm, with 2 concentrations of polymer 6% were obtained and 8% by weight.

El calentamiento por inducción ha sido un método muy utilizado en tratamientos térmicos debido a la reducción en tiempos de calentamiento, sin embargo una gran desventaja es la eficiencia (70% aproximadamente). Debido a ello se han desarrollado concentradores de energía magnética, los cuales son el estudio del presente proyecto. Los concentradores de energía magnética deben de poseer alta permeabilidad magnética inicial, baja fuerza coercitiva, alta saturación magnética y alta resistividad eléctrica; para mejorar la eficiencia, y como consecuencia un ahorro en el consumo de energía eléctrica.En el presente trabajo se obtuvieron materiales compuestos de matriz polimérica obtenidos por compactación uniaxial a seis presiones de compactación que van de 1.5 kPa hasta 9.5 kPa, utilizando polvos de Fe con granulometría de ~7μm y ~109μm, con 2 concentraciones del polímero de 6% y 8% en peso.