In this paper the synthesis and characterization of the metal matrix composite AZ91E Mg-containing 49% ceramic reinforcement of aluminum nitride (AlN) was investigated. The manufacture of this compound was carried through the infiltration method with no external pressure. The starting of a porous preform for AlN green will subsequently be infiltrated with Mg-alloy AZ91E, at a temperature of 850 °C for 12 minutes under argon. Microstructural characterization of the compound was performed by scanning electron microscopy and X-ray diffraction. The results indicate that in the compound Mg-AZ91E/AlN even distribution between the matrix and the ceramic reinforcement is present, by observing the AlN, Mg and Mg17Al12 phase in the microstructure.
En este trabajo se investigó la síntesis y caracterización del material compuesto de matriz metálica Mg-AZ91E con un contenido del 49% de refuerzo cerámico de nitruro de aluminio (AlN). La fabricación de este compuesto se realizó mediante el método de infiltración sin presión externa. Se partió de una preforma porosa en verde de AlN para posteriormente ser infiltrada con la aleación de Mg-AZ91E, a una temperatura de 850°C por 12 minutos en atmósfera de argón. La caracterización microestructural del compuesto se realizó mediante microscopia electrónica de barrido y difracción de rayos-X. Los resultados indican que en el compuesto Mg-AZ91E/AlN se presenta una distribución homogénea entre la matriz y el refuerzo cerámico, observando las fases AlN, Mg y Mg17Al12 en la microestructura.