This research includes the synthesis of metal matrix composites Mg-AZ91E/AlN by capillary infiltration technique at a temperature of 850 °C. In the manufacture of the composites was used as a commercial matrix magnesium alloy AZ91E, and as reinforcement three different samples of AlN powder with particle size of 3 to 9 and 17?m. Aluminum nitride content in the composites was ~ 50% volume; composites were designed with high ceramic content in order to control the thermal expansion and get good thermal conductivity of composites, features required in the proposed applications for these materials.
El presente trabajo de investigación comprende la síntesis de compósitos de matriz metálica Mg-AZ91E/AlN mediante la técnica de infiltración capilar a una temperatura de 850°C. En la fabricación de los compósitos se empleó como matriz una aleación comercial de magnesio AZ91E y como refuerzo tres diferentes muestras de polvos de AlN con tamaño de partícula 3, 9 y 17?m. El nitruro de aluminio contenido en los compósitos fue de ~50% volumen; los compósitos fueron diseñados con alto contenido cerámico con la finalidad de controlar la dilatación térmica y obtener buena conductividad térmica de los compósitos, características requeridas en las aplicaciones propuestas para estos materiales.