Activación mecánica de Al-2Mt, (Mt=Fe, Ca y Zn) y su evaluación en la generación de hidrógeno

Abstract

In this paper, the method of high-energy ball milling was performed to produce alloy systems: Al + Al4Ca, Al + Al13Fe4 and Al (Zn) + Zn (Al). These alloys were reacted to evaluate the rate and amount of hydrogen released with different types of water (sea water, distilled water and tap water). Studies of direct measurements of hydrogen, such as DRX, SEM and EDS indicated that the best results were for the intermetallic system Al + Al4Ca with distilled water and seawater. Similarly, was evaluated the effect of addition of CaO and NaCl in aqueous reaction solutions, the best results (100% hydrogen) were obtained with the addition of NaCl in the Al-Ca system.

En este trabajo, se realizó el procedimiento de molienda mecánica de alta energía, para producir los sistemas de aleación: Al + Al4Ca, Al + Al13Fe4 y Al (Zn) + Zn (Al). Estas aleaciones se hicieron reaccionar para evaluar la velocidad y cantidad de hidrógeno liberado con diferentes tipos de agua (agua de mar, destilada y potable). Tanto los estudios realizados de las mediciones directas de hidrógeno, como DRX, MEB y EDS, señalaron que los mejores resultados obtenidos fueron para el sistema intermetálico Al + Al4Ca con agua destilada y agua de mar. De igual manera, se evaluó el efecto de la adición de CaO y NaCl en las soluciones acuosas de reacción, obteniéndose los mejores resultados (100% de hidrógeno) con la adición de NaCl en el sistema Al-Ca.