In the present work the experimental data obtained by measuring the thermoelectric power (TEP) and the electrical conductivity using Eddy currents (EC) of two high strength low alloy steels is reported, to measure the TEP the hot tip technique was applied and to measure the electrical conductivity the physical phenomenon of electromagnetic induction was used. The material used for this study was obtained of two hot rolled plates of steel with different chemical composition. First, the material was heated to 980°C in an electrical furnace for 30 minutes followed by a water quenching to homogenize grain size and to increase the material hardness. After that, the material was tempered at 400°C, 500°C, 600°C, 700°C, 800°C and 850°C for 30 minutes and air-cooled. The specimens were examined by optic microscopy (OM), scanning electron microscopy (SEM), the TEP and the electrical conductivity were measured, and harness tests were carried out in each specimen, stablishing a direct relation between the TEP and the electrical conductivity with the physic properties developed by the heat treatments. The results of the TEP show a decrease in the values of the absolute TEP in both steels when the temperature of the tempering increases, it was found that the TEP is affected by the grain size, percentage of present phases, precipitation of carbides, the texture and residual stresses, which in conjunction determine the mechanical properties of the material.
En el presente trabajo se reportan los datos experimentales obtenidos al realizar mediciones del potencial termoeléctrico (PTE) y conductividad eléctrica mediante corrientes de Eddy (EC) a dos aceros microaleados, utilizando la técnica termoeléctrica de contacto de la punta caliente y el fenómeno físico de la inducción electromagnética. Las probetas para el estudio fueron obtenidas de dos placas de aceros microaleados laminados en caliente y con diferente composición química. Primeramente se realizaron tratamientos de temple para homogeneizar el tamaño de grano deformado durante el proceso de laminación e incrementar la dureza del material. El temple se realizó a una temperatura de 980°C con un tiempo de permanecía dentro del horno de 30 minutos seguido de un enfriamiento rápido en agua con agitación. Posteriormente se realizaron tratamientos térmicos de revenido a temperaturas de 400°C, 500°C, 600°C, 700°C, 800°C y 850°C con un tiempo de permanecía en el horno de 30 minutos y un enfriamiento lento al aire. Se realizaron: microscopía óptica (MO), microscopia electrónica de barrido (MEB), pruebas de dureza, medición del potencial termoeléctrico y medición de la conductividad eléctrica, estableciendo una correlación directa con las mediciones del PTE y la conductividad eléctrica con las propiedades físicas desarrolladas por los tratamientos térmicos. Los resultados de las mediciones del PTE muestran un decremento en el valor absoluto del PTE en ambos aceros al incrementar la temperatura del revenido, se encontró que el PTE es afectado por el tamaño de grano, porcentaje de fases presentes, precipitación de segundas fases, textura y esfuerzos residuales, los cuales en conjunto determinan las propiedades mecánicas del material en cuestión.