The united front of attack the Bank "Pumpkin" Comanja, Michoacan, Mexico to transladarlo Section's Resistance Materials Laboratory "is sampled Ing. Luis Silva Ruelas "of the Faculty of Civil Engineering of the Universidad Michoacana de San Nicolas de Hidalgo. A representative sample of stone were performed physical and mechanical tests specified in ASTM standards, in triplicate. With data from the physical characterization f'c = 250 kg / cm2 mixed with methods ACI curves and tables Abrams, whichever make the mixture was designed according to ACI. The molds were filled to specification and testing indirect tension and compression were performed on cylindrical specimens at ages 5, 7, 14, 21, 29, 45 days old. The compressive strength was reached late and effort of indirect tension was around ten percent of compressive stress.
Se muestreó el frente único de ataque del Banco “La Calabaza” de Comanja, Michoacán, México para transladarlo a la Sección de Resistencia del Laboratorio de Materiales “Ing. Luis Silva Ruelas” de la Facultad de Ingeniería Civil de la Universidad Michoacana de San Nicolás de Hidalgo. A la muestra representativa de pétreos se le realizaron las pruebas físicas y mecánicas indicadas en los estándares de ASTM, por triplicado. Con los datos de la caracterización física se diseñó la mezcla f’c=250 kg/cm2 con los métodos de curvas de Abrams y tablas ACI, optándose por realizar la mezcla según ACI. Los moldes se llenaron según las especificaciones y las pruebas de tensión indirecta y compresión se realizaron en especímenes cilíndricos a edades de 5, 7, 14, 21, 29, 45 días de edad. La resistencia a compresión se alcanzó tardíamente y el esfuerzo de tensión indirecta fue del orden del diez por ciento del esfuerzo de compresión.