The results of the design of an inorganic-organic coating are presented geopolymeric aimed reduce corrosion in reinforced concrete structures. A concrete mixture was designed by ACI method to achieve high strength fc = 250 kg / cm2, which is used in the manufacture of steel reinforced beams (15cm.x15cm.x30cm.) And concrete cylinders (10cm .x20cm.) without reinforcement. Electrochemical characterization of the beams is shown with anticorrosive coated and uncoated, based on the corrosion rate, and corrosion potential electrical resistivity. Beams, coated and uncoated, were subjected to five cycles of attack Sodium Sulfate (Na2SO4), in order to observe by electrochemical results, such as steel and concrete with each cycle behaves attack. A cylinder was measured the electrical resistivity with a four-point resistometer (Nilsson 400).
Se presentan los resultados obtenidos del diseño de un recubrimiento geopolimérico inorgánico-orgánico cuya finalidad es disminuir la corrosión en estructuras de concreto reforzado. Se diseñó una mezcla de concreto por el método ACI para lograr una resistencia alta f’c = 250 Kg/cm2, la cual es utilizada para la elaboración de vigas reforzadas con acero (15cm.x15cm.x30cm.) y cilindros de concreto (10cm.x20cm.) sin refuerzo. Se muestra la caracterización electroquímica de las vigas, con recubrimiento anticorrosivo y sin recubrimiento, basados en la velocidad de corrosión, potencial de corrosión y resistividad eléctrica. Las vigas, recubiertas y sin recubrir, fueron sometidas a cinco ciclos de ataque de Sulfato de Sodio (Na2SO4), con la finalidad de observar mediante los resultados electroquímicos, como se comporta el acero y el concreto con cada ciclo de ataque. A los cilindros se les midió la resistividad eléctrica con un resistómetro de cuatro puntas (Nilsson 400).