This work shows the behavior of Recycled Concrete at early and middle ages, as the investigation continues. Two different mixtures to make a comparison , one with partial substitution of natural aggregate of which 100 % was recycled gravel and 40% recycled sand , the second in the same way , but adding were developed , based to the experienced, 0.58 % by weight of cement with a fluidizing to reduce the A / C and increase the workability of the concrete, thereby leading to an increase in the mechanical strength of hydraulic concrete made with Portland cement. Cylinders of 10 cm x 20 cm cylinder of 5 cm x 10 cm and beams 15 cm x 60 cm were prepared to the destructive and nondestructive testing . In using the demolition of buildings with concrete reinforced material can be reduced , consequently environmental pollution , as the Portland cement reused, now immersed in substituents aggregates traditional stone was reused , generating less CO2 emissions the atmosphere and reducing operating costs of natural stone aggregates .
Este trabajo muestra el comportamiento del Concreto Reciclado a edades tempranas y medias, ya que la investigación continúa. Se elaboraron dos mezclas diferentes para poder realizar una comparativa, una de ellas con la sustitución parcial del agregado natural de la cual el 100% correspondía a grava reciclada y 40% de arena reciclada, la segunda de la misma forma, pero adicionando, en base a lo experimentado, 0.58% del peso del cemento con un fluidificante para disminuir la relación A/C y aumentar así la trabajabilidad del concreto, provocándose así un aumento de la resistencia mecánica del concreto hidráulico, elaborado con cemento Portland. Se elaboraron cilindros de 10 cm x 20 cm, cilindros de 5 cm x 10 cm y vigas de 15 cm x 60 cm para realizar las pruebas destructivas y no destructivas. Al utilizar el material producto de la demolición de edificaciones a base de concreto armado, puede reducirse, consecuentemente la contaminación ambiental, ya que el cemento Portland reutilizado, inmerso ahora en los agregados sustituyentes de pétreos tradicionales, se reutilizará, generándose menores emisiones de CO2 a la atmósfera y reduciéndose también costos de explotación de agregados pétreos naturales.