The objective of this work is to obtain cellulose pulp from two woods of the genus Eucalyptus: camaldulensis and saligna, by means of the process to the soda. An experimental 3x3 design was applied, with the load factors, with levels of 10, 15 and 19%, and Time, with levels of 30, 40 and 50 minutes. Subsequently applied a factorial design 2² with Load of 10 and 15% and Time of 30 and 40 minutes The cooking temperature was 175 ° C. 100 g of splinter was used dry base, whose size was 3-7 mm thick, 20 mm wide and 25-30 mm long The bath ratio was 4: 1 and the soda concentration was 108 g / L as Na2O. For both species, the conditions that gave better Performance were 10% Load and 30 Minute Time. The E. camaldulensis reached a yield of 42.43% while the E. saligna had a performance maximum of 39.15%. E. camaldulensis obtained a maximum Kappa No. of 22 with the lowest levels of Load and Time, like the E. saligna, whose No. of Maximum Layer was 18.
El objetivo de este trabajo es obtener pulpa celulósica de dos maderas del género Eucalyptus: camaldulensis y saligna, por medio del proceso a la sosa. Se aplicó un diseño experimental 3x3 siendo los factores Carga, con niveles de 10, 15 y 19%, y Tiempo, con niveles de 30, 40 y 50 minutos. Posteriormente se aplicó un diseño factorial 2² con Carga de 10 y 15% y Tiempo de 30 y 40 minutos. La temperatura de cocción fue de 175ºC. Se utilizaron 100 g de astilla base seca, cuyo tamaño era de 3-7 mm de espesor, 20 mm de ancho y 25-30 mm de largo. La relación de baño fue de 4:1 y la concentración de sosa fue de 108 g/L como Na2O. Para ambas especies, las condiciones que dieron mejor rendimiento fueron Carga de 10% y Tiempo de 30 minutos. El E. camaldulensis alcanzó rendimiento de 42.43% mientras que el E. saligna tuvo un rendimiento máximo de 39.15%. El E. camaldulensis obtuvo un No. de Kappa máximo de 22 con los menores niveles de Carga y Tiempo, al igual que el E. saligna, cuyo No. de Capa máximo fue de 18.