In this work the experimental data of the intrinsic sensitivity based on the Seebeck effect, using the technique of thermal contact to detect the presence of texture in specimens of Ti-6Al-4V cold-rolled and annealed reported. The thicknesses employed in the specimens were 1.6 mm, 3.2 mm and 6.4 mm. Specimens were annealed at 760 ° C for 4 hours. Ultrasonic measurements of the velocities of shear waves were conducted and a direct correlation with measurements of PTE was established. PTE results show that in general the annealed specimens (without texture) have lower anisotropy compared with the results obtained for cold-rolled, indicating that there is a better propagation of shear waves. This effect is particularly interesting when applied to specific industrial equipment design.
En este trabajo se reportan los datos experimentales de la sensibilidad intrínseca basada en el efecto Seebeck, mediante la técnica de contacto termoeléctrica para detectar la presencia de textura en especímenes de Ti-6Al-4V rolados en frío y recocidos. Los espesores empleados en los especímenes fueron de 1.6 mm, 3.2 mm y 6.4 mm. Los especímenes fueron recocidos a 760 ºC por 4 horas. Se realizaron mediciones ultrasónicas de las velocidades de las ondas de corte y se estableció una correlación directa con las mediciones del PTE. Los resultados del PTE muestran que en general los especímenes recocidos (sin textura) presentan menor anisotropía comparados con los resultados obtenidos para los rolados en frío, lo cual indica que existe una mejor propagación de las ondas de corte. Este efecto es interesante sobre todo si se aplica al diseño de equipos industriales específicos.