In this research was made a study about of electrochemical corrosion of steel high- strength low-alloy (HSLA), low carbon content is held. The microalloyed steel to be studied was made at the Institute of Metallurgy of the Michoacana University of San Nicholas de Hidalgo; whose chemical composition is: %C= 0.052, %Si= 0.051, %Mn= 1.325, %P= 0.011, % S=0.022, %Cr= 0.675, %Mo= 0.0077, %Ni= 0.005, %Cu= 0.058, %Al= 0.068, %V= 0.061. Also was made a characterization by scanning electron microscopy of the products of the electrochemical corrosion of steel, using a medium of simulated acid rain at room temperature with varying pH = 2, pH = 5 and pH = 8. Within the project it raised obtain the corrosion rate of microalloyed steel under these conditions.
En esta investigación se realizó un estudio sobre el tema de la corrosión electroquímica de un acero de alta resistencia y baja aleación (HSLA), de bajo contenido de carbono. El acero microaleado que se estudió fue fabricado en el Instituto de Metalurgia de la Universidad Michoacana de San Nicolás de Hidalgo; cuya composición química es: %C= 0.052, %Si=0.051, %Mn=1.325, %P= 0.011, %S= 0.022, %Cr=0.675, %Mo= 0.0077, %Ni=0.005, %Cu= 0.058, %Al=0.068, %V= 0.061. Se realizó caracterización mediante microscopía electrónica de barrido de los productos de la corrosión electroquímica del acero, utilizando un medio de lluvia ácida simulada a temperatura ambiente con variaciones de pH= 2, pH= 5 y pH= 8. Dentro del proyecto se planteó obtener la velocidad de corrosión del acero microaleado sometido a estas condiciones.