The unleaded ceramics 0.96 (K0.48Na0.52) 0.95Li0.05Nb0.925MnXSb0.07O3-0.04BaZrO3 were prepared by the conventional solid state method, using different concentrations of Mn. The work carried out focused on the search for new materials to replace lead-based materials, due to the damage they can cause to the environment and living beings, as well as obtaining better properties by inducing the coexistence of phases with the rhombohedral structure. The effects of Mn on structure, microstructure, electrical and high power properties were investigated. The experimental results of lead-based ceramics show good results, indicating that these materials are a promising candidate for the replacement of lead-based materials, for the benefit of the environment.
Se prepararon las cerámicas sin plomo 0.96(K0.48Na0.52)0.95Li0.05Nb0.925MnXSb0.07O3-0.04BaZrO3 por el método convencional de estado sólido, utilizando diferentes concentraciones de Mn. El trabajo realizado se enfocó en la búsqueda de nuevos materiales para la sustitución de materiales a base de plomo, debido a los daños que pueden provocar al medio ambiente y seres vivos, así como obtención de mejores propiedades induciendo la coexistencia de fases con la estructura romboédrica. Se investigaron los efectos del Mn sobre la estructura, microestructura, propiedades eléctricas y de alta potencia. Los resultados experimentales de las cerámicas a base de plomo muestran buenos resultados, lo que indica que estos materiales son un candidato prometedor para la sustitución de materiales a base de plomo, en beneficio del medio ambiente.