In the present work, the synthesis and characterization of a metallic foam of Ti-Ta-Sn without and with carbon nanotubes was developed, the effect that carbon nanotubes have on the alloy, obtained by mechanical mixing with different porosities (0, 30 and 40% wt). The synthesis of carbon nanotubes was carried out using the Chemical Vapor Deposition (CVD) method. temperature curve for each case. The alloys were characterized by density, X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), destructive and non-destructive mechanical tests (Nanoindentation, microhardness, ultrasound and compression). Finally, the alloys were subjected to corrosion by the electrochemical method submerged in Hank's solution and Saliva Solution.
En el presente trabajo se desarrolló la síntesis y caracterización de una espuma metálica de Ti-Ta-Sn sin y con nanotubos de carbono, se analizó el efecto que tienen los nanotubos de carbono en la aleación obtenida por mezcla mecánica con diferentes porosidades (0, 30 y 40% wt). La síntesis de los nanotubos de carbono se realizó mediante, el método de Deposición Química del Vapor (CVD) por sus siglas en inglés. La sinterización de la espuma de aleación Ti-Ta-Sn se realizó un tratamiento térmico en un horno convencional programado una curva de temperatura para cada caso. Las aleaciones se caracterizaron mediante densidad, difracción de rayos X (DRX), microscopia electrónica de barrido (MEB), espectroscopia de energía dispersiva (EDS), Se realizó pruebas Mecánicas destructivas y no destructivas (Nanoindentación, microdureza, ultrasonido y compresión). Finalmente, las aleaciones fueron sometidas a corrosión por el método electroquímico sumergidas en solución Hank´s y Solución Salival.