In the present work we study, hydrodenitrogenation (HDN) and hydrodesulfurization (HDS) reactions of primary light gas oil (GLP) fractions are studied, using a NiMoW/- Al2O3-based trimetallic catalyst. The catalytic activity and selectivity of the system are evaluated using 10 fractions obtained in the distillation of GLP, which contain different concentrations of sulfur and nitrogen. The reactions are carried out in a batch stainless steel reactor, operating at conditions of temperature and pressure alike to those used in hydrotreating systems on an industrial scale. In the present work, the hydrodenitrogenation (HDN) and hydrodesulfurization (HDS) reactions of primary light gas oil (LPG) fractions were studied, using a trimetallic catalyst based on NiMoW/ƴ-Al2O3. The catalytic activity and selectivity of the system are evaluated using 10 fractions obtained in the distillation of LPG, which contain different concentrations of sulfur and nitrogen. The reactions are carried out in a stainless-steel batch reactor, operating at temperature and pressure conditions similar to those used in industrial-scale hydrotreating systems. The impregnation of the active phases was carried out by the method of incipient pore filling, maintaining a concentration of 2.5% by weight of NiO, 6% by weight of MO3 and 9.7% WO3 in the catalyst. The characterization of the support and prepared catalyst was carried out using the following techniques: N2 physisorption, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Infrared spectroscopy (IR), Raman spectroscopy and UV-Diffuse Reflectance. VIS. The results of the catalyst characterization techniques show that the materials present a good dispersion of the active phases or, the possible crystals formed are smaller than 4 nm which cannot be detected by the equipment. the XPS results indicate the presence of Ni+2 (Ni(OH)2) and Mo+6 (MoO3).
En el presente trabajo se estudió las reacciones de hidrodesnitrogenación (HDN) e hidrodesulfuración (HDS) de fracciones de gasóleo ligero primario (GLP), utilizando un catalizador trimetálico a base de NiMoW/ƴ-Al2O3. Se evalúa la actividad catalítica y la selectividad del sistema utilizando 10 fracciones obtenidas en la destilación de GLP, que contienen diferentes concentraciones de azufre y nitrógeno. Las reacciones se llevan a cabo en un reactor de acero inoxidable por lotes, operando a condiciones de temperatura y presión similares a las utilizadas en sistemas de hidrotratamiento a escala industrial. La impregnación de las fases activas se realizó por el método de incipiente llenado de poro, manteniendo una concentración de 2.5 % en peso de NiO, 6 % en peso de MO3 y 9.7 % WO3 en el catalizador. La caracterización del soporte y Catalizador preparado fue llevada a cabo mediante las siguientes técnicas: Fisisorción de N2, Difracción de rayos X (DRX), Espectroscopía fotoelectrónica de rayos X (XPS), Espectroscopía infrarroja (IR), Espectroscopia Raman y Reflectancia Difusa UV-VIS. Los resultados de las técnicas de caracterización del catalizador muestran que los materiales presentan una buena dispersión de las fases activas o bien, los posibles cristales formados son de un tamaño menor a 4 nm los cuales no alcanzan a ser detectados por el equipo. los resultados de XPS nos indican la presencia de Ni+2 (Ni(OH)2) y Mo+6 (MoO3).
